耐油型辐照交联无卤低烟阻燃聚烯烃塑料
Oil-resistant irradiation cross-linkable non-halogen low-smoke flame-retardant polyolefin compounds
性能
Property
单 位
Unit
3605
3625
规定值
Specified value
典型值
Typical value
规定值
Specified value
典型值
Typical value
老化前 Without ageing
拉伸强度 tensile strength
MPa
min. 9.0 15.7
min. 9.0 12.3
断裂伸长率elongation at break
%
min. 125
230 min. 125
210 老化后 After ageing in air oven
温度 temperature
℃
135±2
135±2
158±2
158±2
时间 duration
h
168
168
168
168
老化后拉伸强度
tensile str. after ageing
MPa
--
17.6
--
14.7
拉伸强度变化率
variation at tensile strength
%
max. ±30 +12
max. -20 +20 老化后断裂伸长率 elongation after ageing
%
min. 100 196
min. 100 225
断裂伸长率变化率
variation at elongation
%
max .±30 -14
max. -40 +6
耐矿物油
Immersion in lubricating-oil
浸油温度oil temperature
℃
100 100 100 100 浸油时间duration
h
24
24
70 70 拉伸强度变化率
variation at tensile strength
%
max. ±40 -26
max. -50 -32
断裂伸长率变化率
variation at elongation
%
max. ±40 -17
max. -50 -2
耐燃料油Immersion in fuel oil
浸油温度oil temperature
℃
--
70 70 70 浸油时间duration
h
--
168
168
168
拉伸强度变化率
variation at tensile strength
%
--
-39
max .-55
-38
断裂伸长率变化率
variation at elongation
%
--
-27
max. -55
+1
低温性能
Bevaviour at low temperature
冷冲击温度 cold impact temperature
℃
-30 通过
-30 通过
20℃体积电阻率
Volume resistivity at 20℃
Ω·m
--
5×1013
--
2×1013
介电强度 Dielectric strength
MV/m
min. 20 29
min. 20 28
热延伸试验 Hot set at 200℃
热负荷延伸率
Elongation under load
%
max. 175
10 max. 175
15
永久变形Permanent elongation after cooling
%
max. 250max. 250卤酸气体释出量Acid gas emission
mg/g
max. 5
<1
Max. 5
<1
pH值
min. 4.3
6.8
min. 4.3
6.5
电导率 Conductivity
μs/mm
max. 10 1.2
max. 10 1.5
最大烟密度（有焰）
Smoke density(flaming)
max. 10